Popular Economical Heat Resistance O Ring EPDM 30 - 90 Shore Hardness
Our O-Ring Advantages
1. O-Rings offer an efficient and economical sealing element for a wide range of static or dynamic applications.
2. O-Ring sizes are defined by the inner diameter-ID and the cross section-CS , our o-ring Inner Diameter can be from 0.5mm to 1500mm .
3. Standard sizes such as AS568(PARKER sizes), JIS(P TYPE,G TYPE,S TYPE ,V TYPE ,F TYPE sizes) , BS1516 sizes Metric sizes as well as non-standard sizes are all avaiblabe.
4. We have more than 2000 o-ring mould toolings , so you could get any size here without set-up or tooling charge . Huge inventory of o-rings can meet your urgent requiremnets.
5. A very wide range of elatomer material can be selected , main material: NBR(BUNA-N,Nitrile) , FKM(FKM) , Silicone(VMQ) ,HNBR, FFKM ,EPDM , PU(Polyurethane , urethane),Fluorosilicone(FVMQ),Neoprene(CR) and so on. Hardness of material can be from 40 ShoreA(Durometer) to 90 ShoreA(Durometer)
O-Ring Technical requirements:
Appearance meets GB/T3452.2-2007 Material meets HG/T2579-2008 Size meets GB/T3452.1-2005
In additon , all our products are ROHS and REACH Compliant (we mainly export products to USA and Europe market).
O-Ring Features :
1. Good sealing solution , long service life .
2. Easy installation reduces risk .
3. Working in various medium based on different elastomer material.
| Press Cure | Post Cure | ||
| Sheet : 5min 170℃ | Sheet : 1 hrs 125℃ | ||
| Button : 10 min 170℃ | Button : 1 hrs 125℃ | ||
| ORIGINAL PROPERTIES | SPECIFICATION | TEST RESULT | |
| HARDNESS SHORE A | 70°±5 | 70 | |
| TENSILE STRENGTH, MPA, MIN | 14 | 14.9 | |
| ULTIMATE ELONGATION, ％, MIN | 300 | 327 | |
| SPECIFIC GRAVITY (g/cm3) | 1.15 | ||
| HEAT RESISTANCE 70 H . AT 100℃ | |||
| CHANGE IN HARDNESS, POINTS | 10 | 2 | |
| CHANGE IN TENSILES STRENGTH,% | -25 | -4.1 | |
| ULTIMATE ELONGATION,MAX % | -25 | -3.4 | |
| COMPRESSION SET, MAX, 22H AT 70℃ | 25 | 8 | |
| RESISTANCE TO OZONE | |||
| EXPOSURE METHOD B | N0 CRACK | PASS | |
| WATER RESISTANCE:100℃,70H (EA14) | |||
| VOLUME CHAGE,% | ±5 | 3.7 | |
| LOW-TEMPERATURE BRITTLENESS NONBRITTLE | |||
| AFTER 3MIN AT -55°C (F19) | NONBRITTLE | PASS | |