Universal Coloured FKM O Rings Sealing , Heat Resistant O Ring AS568
Trade Names:
ASTM D1418 Designation: FKM
ASTM D2000/SAE Type, Class: HK
ORK Compound Designation: VT
Standard Color: Black
Description: Combining high temperature resistance with outstanding chemical resistance, Fluorocarbon-based compounds approach the ideal for a universal O-ring material.
Key Use(s): Seals for aircraft engines. Seals for automotive fuel handling systems. High temperature/low compression set applications. Wide chemical exposure situations. Hard vacuum service.
Temperature Range
Standard Compound: -13° to +446°F
Special Compound: -40° to +446°F
Hardness (Shore A): 55 to 90.
Features: High fluorine grades offer higher resistance to swell in high octane and oxygenated fuel blends. This give superior performance in Ethanol/Methanol blended gasoline. Base resistant grades offer improved resistance to amine based oil protectants found in new transmission oils. Also, improved resistant to steam for higher temperature services. Low temperature bases can improve performance to -40°F.
New Polymers being offered have improved chemical resistance and low temperature performance.
FKM® Extreme™ ETP offers similar chemical compatibility as Kalrez™ with temperature performance with a TR(10) of -40°F and brittleness to -76°.
Limitations: Fluorocarbons (FKM®s) are not recommended for exposure to ketones, amines, low molecular weight esters and ethers, nitro hydrocarbons, hot hydrofluoric or chlorosulfonic acids, or Skydrol® fluids. They are also not recommended for situations requiring good low temperature flexibility.
| NBR 70 TEST REPORT ASTM D2000 M2BG 714 B14 EO14 EF11 EF21 EA14 F17 | |||
| PROPERITIES | SPECIFICATION | TEST RESULT | TEST METHOD |
| Hardness shore A | 70±5 | 72 | D2240 |
| Tensile MPA Min | 14 | 14.5 | D12 |
| Elongation % Min | 250 | 315 | D412 |
| Gravity |
| 1.263 | D297 |
| Heat resistant 70h 100℃ Hardness change | ±15 | ﹢5 | D573 |
| Tensile strength% | ±30 | ﹢15 |
|
| Elongation Max | -50 | -12 |
|
| Compression Max 22h at 100℃ | 25 | 14 | D395 |
| NO1 oil resistant |
|
|
|
| Change in hardness | -10~+5 | +1 | D471 |
| Change in tensile Max | -25 | -16 |
|
| Change in Elongation | -45 | -20 |
|
| Change in Volume% | 0~25 | +6 |
|
| Fuel resistant 70 H at 23℃ |
|
|
|
| Hardness change | ±10 | +3 | D471 |
| Tensile change Max | -25 | -8 |
|
| Elongation change Max | -25 | -10 |
|
| Change in Volume | -5~+10 | +3 |
|
| Water Resistant |
|
| D417 |
| Change in Hardness |
| +3 |
|
| Change in tensile |
| +5 |
|
| Change in Elongation |
| -14 |
|
| Change in Volume | ±15 | +3 |
|
| Low Temperature resistant |
|
| D2137 |
| 3 MIN -40℃ | Non brittle | Pass | D2137 |